It appears that you are currently in USA.
- zirconia-reinforced, high-strength glass ceramic generation
- available as monochromatic blanks in two translucency levels (T, HT)
VITA SUPRINITY® PC
Glass ceramic. Revolutionized.
- high reliability thanks to a zirconia-reinforced glass ceramic matrix
- precision-fit results thanks to material blanks with high edge stability
- simple processing thanks to good polishing characteristics and high firing stability
- brilliant esthetics thanks to integrated translucency, opalescence and fluorescence
Recommended indications*
Various (esthetic) options, thanks to a wide indication range:
- Posterior crown
- Anterior crown
- Implant-supported crown
- Veneer
*) These are recommended indications; the entire range of single tooth restorations can normally be fabricated. For details, please refer to the respective working instructions of the products.
- VITA classical A1-D4®, high translucent (HT)
A1, A2, A3, A3.5, B2, C2, D2 - VITA classical A1-D4®, translucent (T)
A1, A2, A3, A3.5, B2, C2, D2 - VITA SYSTEM 3D MASTER®, high translucent (HT)
0M1, 1M1,1M2, 2M2, 3M2, 4M2 - VITA SYSTEM 3D MASTER®, translucent (T)
0M1, 1M1,1M2, 2M2, 3M2, 4M2
Blocks (mm):
- PC-14 (12 x 14 x 18)
VITA SUPRINITY® PC products
VITA SUPRINITY® PC VITA SYSTEM 3D-MASTER
| Description | Prod. no. 5 pcs. |
|---|---|
| 0M1-T, PC-14 |
EC4S010001 12 x 14 x 18 mm |
| 1M1-T, PC-14 |
EC4S010004 12 x 14 x 18 mm |
| 1M2-T, PC-14 |
EC4S010005 12 x 14 x 18 mm |
| 2M2-T, PC-14 |
EC4S010009 12 x 14 x 18 mm |
| 3M2-T, PC-14 |
EC4S010016 12 x 14 x 18 mm |
| 4M2-T, PC-14 |
EC4S010023 12 x 14 x 18 mm |
| 0M1-HT, PC-14 |
EC4S010101 12 x 14 x 18 mm |
| 1M1-HT, PC-14 |
EC4S010104 12 x 14 x 18 mm |
| 1M2-HT, PC-14 |
EC4S010105 12 x 14 x 18 mm |
| 2M2-HT, PC-14 |
EC4S010109 12 x 14 x 18 mm |
| 3M2-HT, PC-14 |
EC4S010116 12 x 14 x 18 mm |
| 4M2-HT, PC-14 |
EC4S010123 12 x 14 x 18 mm |
VITA SUPRINITY® PC VITA classical A1-D4®
| Description | Prod. no. 5 pcs. |
|---|---|
| A1-T, PC-14 |
EC4S010030 12 x 14 x 18 mm |
| A2-T, PC-14 |
EC4S010031 12 x 14 x 18 mm |
| A3-T, PC-14 |
EC4S010032 12 x 14 x 18 mm |
| A3.5-T, PC-14 |
EC4S010033 12 x 14 x 18 mm |
| B2-T, PC-14 |
EC4S010036 12 x 14 x 18 mm |
| C2-T, PC-14 |
EC4S010040 12 x 14 x 18 mm |
| D2-T, PC-14 |
EC4S010043 12 x 14 x 18 mm |
| A1-HT, PC-14 |
EC4S010130 12 x 14 x 18 mm |
| A2-HT, PC-14 |
EC4S010131 12 x 14 x 18 mm |
| A3-HT, PC-14 |
EC4S010132 12 x 14 x 18 mm |
| A3.5-HT, PC-14 |
EC4S010133 12 x 14 x 18 mm |
| B2-HT, PC-14 |
EC4S010136 12 x 14 x 18 mm |
| C2-HT, PC-14 |
EC4S010140 12 x 14 x 18 mm |
| D2-HT, PC-14 |
EC4S010143 12 x 14 x 18 mm |
VITA SUPRINITY® PC UNIVERSAL VITA SYSTEM 3D-MASTER®
| Description | Prod. no. 5 pcs. |
|---|---|
| 0M1-T, PC-14 |
EN1S03024445 12 x 14 x 18 mm |
| 0M1-HT, PC-14 |
EN1S04024445 12 x 14 x 18 mm |
VITA SUPRINITY® PC UNIVERSAL VITA classical A1-D4®
| Description | Prod. no. 5 pcs. |
|---|---|
| A1-T, PC-14 |
EN1S03364445 12 x 14 x 18 mm |
| A2-T, PC-14 |
EN1S03374445 12 x 14 x 18 mm |
| A3-T, PC-14 |
EN1S03384445 12 x 14 x 18 mm |
| A3.5-T, PC-14 |
EN1S03394445 12 x 14 x 18 mm |
| B2-T, PC-14 |
EN1S03424445 12 x 14 x 18 mm |
| C2-T, PC-14 |
EN1S03464445 12 x 14 x 18 mm |
| D2-T, PC-14 |
EN1S03494445 12 x 14 x 18 mm |
| A1-HT, PC-14 |
EN1S04364445 12 x 14 x 18 mm |
| A2-HT, PC-14 |
EN1S04374445 12 x 14 x 18 mm |
| A3-HT, PC-14 |
EN1S04384445 12 x 14 x 18 mm |
| A3.5-HT, PC-14 |
EN1S04394445 12 x 14 x 18 mm |
| B2-HT, PC-14 |
EN1S04424445 12 x 14 x 18 mm |
| C2-HT, PC-14 |
EN1S04464445 12 x 14 x 18 mm |
| D2-HT, PC-14 |
EN1S04494445 12 x 14 x 18 mm |
VITA SUPRINITY® PC kits
VITA SUPRINITY® PC VITA SYSTEM 3D-MASTER
EC4S0STSETC3D
| Quantity | Content | Material |
|---|---|---|
| 12 | PC | inLab 0M1-HT, 1M1-HT, 1M2-HT, 2M2-HT, 3M2-HT, 4M2-HT, 0M1-T, 1M1-T, 1M2-T, 2M2-T, 3M2-T, 4M2-T |
| 1 | 75 ml | VITA AKZENT Plus GLAZE LT Spray |
| 1 | Firing tray W for crowns and bridges | |
| 1 | 2 Platinum pins (1 anterior and 1 posterior pin) | |
| 1 | VITA SUPRINITY Polishing Set clinical |
EC4S0STSETT3D
| Quantity | Content | Material |
|---|---|---|
| 12 | PC | inLab 0M1-HT, 1M1-HT, 1M2-HT, 2M2-HT, 3M2-HT, 4M2-HT, 0M1-T, 1M1-T, 1M2-T, 2M2-T, 3M2-T, 4M2-T |
| 1 | 75 ml | VITA AKZENT Plus GLAZE LT Spray |
| 1 | Firing tray W for crowns and bridges | |
| 1 | 2 Platinum pins (1 anterior and 1 posterior pin) | |
| 1 | VITA SUPRINITY Polishing Set technical |
VITA SUPRINITY® PC VITA classical A1-D4®
EC4S0STSETC
| Quantity | Content | Material |
|---|---|---|
| 16 | PC | inLab A1-T - 0M1-HT |
| 1 | 75 ml | VITA AKZENT Plus GLAZE LT Spray |
| 1 | Firing tray W for crowns and bridges | |
| 1 | 2 Platinum pins (1 anterior and 1 posterior pin) | |
| 1 | VITA SUPRINITY Polishing Set clinical |
EC4S0STSETT
| Quantity | Content | Material |
|---|---|---|
| 16 | PC | inLab A1-T - 0M1-HT |
| 1 | 75 ml | VITA AKZENT Plus GLAZE LT Spray |
| 1 | Firing tray W for crowns and bridges | |
| 1 | 2 Platinum pins (1 anterior and 1 posterior pin) | |
| 1 | VITA SUPRINITY Polishing Set technical |
VITA SUPRINITY PC – SYSTEM SOLUTIONS*
VITA offers VITA SUPRINITY PC with specific holder systems for the CAD/CAM systems:
- CEREC/inLab (Dentsply Sirona)
- PlanMill 40/PlanMill 40S/PlanMill 50S (Planmeca)
- MyCrown Mill (FONA Dental s.r.o.)
- Ceramill mikro IC/CeramillMotion 2/Ceramill Matik (Amann Girrbach AG)
VITA SUPRINITY PC – UNIVERSAL SOLUTIONS*
VITA offers VITA SUPRINITY PC with universal holder system for the CAD/CAM systems:
- CS 3000/CS 3100 (Carestream Dental, Inc)
- DMG ULTRASONIC Serie (DMGMori AG)
- CORiTEC Serie (imes-icore GmbH)
- Röders RXD Serie(Röders GmbH)
- N4/R5/S1/S2/Z4 (vhf camfacture AG)
- MILLING UNIT M Serie (Zirkonzahn S.r.l.)
- DGSHAPE DWX-4W(DGSHAPE Corporation)
- Zfx Inhouse5x (Zfx GmbH)
*) Note: The range of VITA CAD/CAM material versions/geometries/shades available may vary for individual CAD/CAM system partners or systems. The hardware and software requirements in each case are available from the respective CAD/CAM system partners.
Easy download for multiple documents
Download a .zip file containing all the selected files in a single step.Simply tick the files then click here.
What stains can be used to characterize VITA SUPRINITY PC restorations and what is the exact procedure in this case?
- VITA AKZENT Plus stains, available as POWDER, PASTE or SPRAY, and glaze material, are applied to the restorations after full anatomical milling has been completed. Characterization using Effect Stains and Body Stains and glaze material can be performed either in combination with or following crystallization firing.
What is of particular importance when customizing VITA SUPRINITY PC restorations? What needs to be taken into consideration during processing?
- With the cut-back technique, incisal or occlusal reduction is performed to allow for layering using the VITA VM 11 materials that have been optimally adapted for this purpose. Thanks to the outstanding surface wettability, layering can be applied directly without liner firing or washbake. The minimized application of ceramic materials adapted in terms of shade facilitates highly-esthetic restorations in just a few steps.
What firing units are required for thermal firing and what must practice offices and laboratories observe in this regard?
- The restorations can be crystallized in any vacuum furnace that supports slow cooling. Honeycomb firing trays with platinum pins are the most suitable for firing. No particular aids are required, and as a result of the superior firing stability of the base material, firing paste is not required either; it can, however, be used additionally in the fabrication of a custom firing tray.
How should VITA SUPRINITY PC restorations be polished, and what polishing tools should be used?
- Reworking should only be performed using fine-grained diamond-coated milling tools (4 μm) and special polishing tools (for pre-polishing: diamond finishing bur / 8 μm) at low pressure. For optimum polishing, a 2-phase polishing range for extraoral and intraoral use has been specially developed, which allows a natural highgloss finish to be achieved quickly and easily using the VITA SUPRINITY Polishing Set technical and clinical.